It is a common mistake that when you work with Damascus, the risk of extinction - the layers of separation - is just what you should do. Never put acid in the microwave! I've personally gone as high as 6-1 dilution with ferric, but that took literally hours to obtain the depth of etch I wanted. to 2 parts Hydrogen Peroxide (the common 3% kind that's sold in dollar stores & drugstores for $0.50 a pint) Warning!!!!! It is commonly used to etch steel and stainless steel parts, but it is also capable of etching copper. That's where I just got a bottle, $14.59 for a quart. The classic non-press method is to make a fairly high layer bar and then either drill it full of shallow holes that almost touch and onlygo about a third of the way through the bar OR punch those holes with a broad pointed punch, then forge the bar flat until the holes are at surface level. You can now pay for your purchase with 4 interest free installments. This prepares your steel for an even etch. Warm your acid to room temperature. We are exploring additional options of engraving and will let you know when those are available. Remember to wear safety goggles and gloves at all times. In a large nonmetallic bowl or container, mix 1 part hydrochloric acid with 2 parts hydrogen peroxide. After 10 minutes take it out and give it a quick dip in the bucket of water. -- Theodore Roosevelthttp://stephensforge.com. You can repeat 5 and 6 steps for a deep etch if you wish. #5. You will also need to wash a baking bar. Step 2. So less about etching and more about patterns, how does one make raindrop damascus? Hydrochloric acid is a purer and more toxic form of muriatic acid. Etching Concrete: The Process. No idea if I'm doing something wrong or if its just part of using vinegar ir if I'm just bad at putting metal into liquids. Start very dilute, like 1:10 or 1:20. This is how I do it and it works for me. Ferric Chloride is an iron "salt" of HCl that is nonetheless very acidic, though not as "strong" as HCl. Damascus etching is completed with either ferric chloride or muriatic acid. Follow Leave the copper blank in the solution for at least half an hour. It truly is one of the best, if not the best, stainless damascus steel in the world. In other words, it is a mixture of ferric and cupric chlorides that is renewable effectively forever. Toss the PCB into the solution and itll take off. Swishing the steel around in the etch to break up the bubbles is not a bad idea either. Remove your Damascus piece from acids and throw it to your baking board for 5 minutes to reduce acids. If too late.no problem that is how we learn. on Step 8. Step 1: What You Need Some damascus steel Etchant - Ferric Chloride (strength 42 baume) Distilled water Acetone Glass or plastic containers Extra fine (000) steel wool Wire (to hang piece in acid) Bucket of water Rubber gloves Baking soda oil (I used olive oil as the knife will be used on food) Ask Question Comment Step 2: Clean I dont own any Damascus and this is my first, so is that normal? Eliminates the need to use harsh chemicals, provides a safer work enviornment . For etching, you'll find a confusing array of products, including standard muriatic acid as well as products such as Klean-Strip Green Muriatic Acid ($7.84 per gallon at Home Depot) and. Cheers Johnno 1. Weapons made from Damascus steel are vastly superior to weapons formed from iron! For this reason, true Damascus steel is called wootz Damascus steel to distinguish it from imitations. Warm acid gives a much faster etch, but then you get less time to control what's happening. Muriatic acid will strip the galvanizing off, Ospho, which is phosphoric acid can be used to etch the zinc to get the paint to stick, it is also a 'rust reformer' changing ferric oxide 'rust' to phosphoric oxide, which is stable and can be painted with out worry about latter rusting. ( Etching Damascus - Mike Carter demonstrates how to acid etch Damascus knife blades to reveal the pattern in the steel; How do I heat-treat my 1075 or 0-1 Carbon Damascus billet? Muriatic Acid vs. Hydrochloric Acid Etching is used to make circuit boards, where a thin copper sheet is selectively dissolved away to form a path for electricity. Furthermore if forged in the correct manner you can make swords from it that depicts a pattern often likened to watered silk. We are limited on the number of characters that can be used as the knives vary in size. Etching a stainless damascus steel knife (or any damascus) is not as complicated as many people tend to believe. Actually, the process of efflorescence removal discussed above also etches the masonry. Your email address will not be published. [woocommerce-login-nonce] => Many hand-forged Damascus blades are made out of high carbon steel with small amounts of chromium in the alloy. Mine is stronger :-),

Gerald Boggs

. Wash your piece with alcohol and pat it dry with a clean rag. How To Acid Etch Metal With Vinegar The Art Of Weapons. It is in a greatly reduced concentration compared to the 30% hydrochloric acid (muriatic acid). Then sanded to 400 grit, I took the Muriatic Acid from the bottle that was 32% strong as the bottle says and placed 24 oz of water in a plastic tub, I then added the acid about 8 oz . Etching acids can range from powerful hydrochloric or sulfuric acid to much weaker acids even household vinegar, citrus fruit, or mustard can be used effectively. this makes Ferris chloride, you need to add hydrogen peroxide to convert to ferric , go slow in an over large container is is an energetic reaction the ferris will be a green color, add peroxide until it turns brown and it is ferric, add distilled water until it etches nicely. No need to go full strength to get results. Put on your protective gear. Then I remembered I'd been thinking of switching to re-usable etchant, created on the bench using muriatic acid (the store name for hydrochloric acid, HCl, used for cleaning swimming pools). Damascus etching is completed with either ferric chloride or muriatic acid. 4 years ago Everything you need to know about ChatGPT. Blotchiness in an etch is usually the result of oil somewhere in the system, either on the blade or in the etchant. It will also make everything steel in the same room with it rust. Learn More, click here. You can use some 2000 grit sandpaper at this stage to very lightly sand it to bring out the shine on the shiny steel. File away any burrs on the side of the steel you plan to etch with acid. Edit* I just realized folks already gave this answer. It is an ultra high carbon steel that achieved liquid state which should, theoretically, allow you to get a homogeneous steel product with equal carbon distribution and no slag inclusions at all. and wear gloves, eye protection, and clothing. While high in carbon steel, the blade can easily rust if not cared for. You are using an out of date browser. I was wondering about the thoughts of cold or rust blui Requests: Array Works great. Forseti Steel is a fairly new company that imports what appear to be high quality, handmade knives from Pakistan. Does etching have to be done before temper, or can you etch first and have the pattern survive the process? Share Save Helvetica Comment CaiLei 3 years ago Follow It is an ultra high carbon steel that achieved liquid state which should, theoretically, allow you to get a homogeneous steel product with equal carbon distribution and no slag inclusions at all. You can also use Windex with this step, but do not try to break your piece. If you decide that you want to reverse one another, you can also make a quick frame by placing your teaspoon refined in acid for a few minutes and then entering a baking soda. Is the pattern deep enough? Very clean. Damascus steel is a famed type of steel recognizable by the watery or wavy light and dark pattern of the metal. Your email address will not be published. If the reaction is proceeding too slowly for your liking you can heat up the mixture. With ferric acid, keep grit between 400 and 600. Over the years, Damascus1 has produced various products using one of the four hairdressers of the nazel hair. I've been there before.. Neutralize the acid and Lightly sand the oxides off with scotch bright or 2000/3000 grit sand paper and re etch (don't touch it with your fingers). Sprinkle the mixture evenly across the surface of the prepared concrete. How long does ferric chloride take to etch? Is it possible to etch Damascus with muriatic acid? Once you have gathered all the necessary supplies and safety gear, you will be ready to begin etching your garage floor. It will certainly freeze being significantly water. I etch pretty deeply (3-4 soaks at 15-20 minutes, scrubbing oxides off between soaks) then a light buffing with pink scratchless rouge to bring out the contrast. Place your board to be etched in your new solution and watch it go! It still retains enough corrosive quality to etch your steel blades. rideable.org is a participant in the Amazon Services LLC Associates Program, an affiliate advertising program designed to provide a means for sites to earn advertising fees by advertising and linking to amazon.com. Add clean, clear water to a plastic bucket. It needs to be heated on a hot plate or in a crock pot first. After being etched the blank can be polished to give a stepped or contrasting look. I degrease with multiple wipes of acetone on new paper towels each time, but some guys prefer dish soap and water or alcohol. Before you begin, check the expiration date on your acid of choice to be sure that it's not too old. 3 years ago Begin the etching process. 3D Printed Futuristic Space Age Wall Clock. Mix this stuff 4:1 with distilled water. Suspend your piece in the acid. hey guys, i used the lovely search function with pretty much no results. Bring your Damascus at the end of grit 400 to 600. You can do this by first mixing a small solution in your watering can starting at a 5:1 ratio. After heat treating, bring your Damascus to a 400 to 600 grit finish. If you use muriatic acid, you can bring Damascus up to 1200 grit, or you can leave it 400 grit. Joshua C States. As with all chemicals, make sure you are wearing the appropriate protective clothing and gear. Each Damascus Steel ring is uniqueno two designs will look exactly alike. I do Oh well, looks like another one for the personal collec Thats one of them there corner daggers Essentially you forge weld 2 contrasting types of steel (I used 15N20 and 75Ni8) then manipulate it to make a pattern. You can also make it, by adding Fe to HCl. I know at least one ABS Mastersmith that used muriatic acid to etch then blue their bladeshe doesn't much care for Floric Chlorideit isn't deep enough. I know the website says not to mix it but we're also not using it to make custom circuit boards Here is a link to some interesting information regarding concentrations Chemistry, Martial Arts, Mathematics, Woodworking, and Hot Steel, http://www.geraldboggs.com">www.geraldboggs.com

. Coffee Etching Damascus Steel | Knife Making How To/Tip. *Amazon and the Amazon logo are trademarks of Amazon.com, Inc, or its affiliates. Mix baking soda with distilled water, using a lot of cooking soda so you can dip your piece to reduce acids and stop acne action. . Each time acid is added, it will eat away at the travertine. The keys are "pretty dilute" and "multiple, short immersions". The iron will start reacting with the acid to produce hydrogen gas and ferrous chloride. The stronger the acid, the more damage will be done. 3:1, 4:1, or 5:1 distilled water to the FeCl are all commonly used dilutions. The pattern should be looking good. Acid Etch: Disassemble your knife, and thoroughly clean and dry the part you're going to etch (blade, handle, or clip). American Bladesmith Society bladesmiths represent the cutting edge of forged blade performance and design on six continents. I did a simple twist as I like the way it looks. 5. However by simply etching the look will not be correct for gun barrels, and will be a relatively light contrast. No neutralizing step after etching. Damascus Etching. Coffee Etching Damascus Steel | Knife Making How To/Tip Coffee Etching Damascus Steel | Knife Making How To/Tip Watch on You can etch stainless steel, mild steel, or high-carbon steel. Buy NANFANG BROTHERS Damascus Kitchen Knife Set, 14 Pieces Japanese Knife Set Kitchen Knife Set with Block Wooden, 67 Layers VG10 Damascus Steel Chef Knife Set with Sharpener, Sharp Blades at Amazon UK. Apparently this neutralises the piece as well as helping to set the oxides. How do you prepare ferric chloride solution for etching? It's not the only way. They dedicate their customers to the unique inspired world patterns around us, for example, raindrops, razor cords, and baskets. What kind of acid do you use to etch a knife? Advice? The difference between steel metals creates those different ways, especially when used again. Dont touch it with your hands. For example, steel can be etched with hydrochloric acid, nitric acid, or sulfuric acid. 8. These chemical compound work faster than acids. It will rust almost immediately if you don't. The strength of the acid generally determines how quickly the steel will be etched, the stronger the acid, the faster the process. Nitric Acid - mixture of 5 - 10% nitric acid with the balance being alcohol. How do I heat-treat 3V/CPM-154 Damascus billet? I've heard lots of different solution strengths, but 3 parts distilled water to 1 part fecl has worked well for me. From his going on, they have respected their way of access, guided their response, expanded their product line and re-evaluated their unique iDascation process. Put a tablespoon or so of baking powder in a saucepan of water and boil the piece for 10 minutes. You can also use it to clean soot from fireplace bricks. For Sale: Custom & Semi Production Knives (Dealer), KnifeMaker's Market: Knives & More for Sale, Wanted: Knifemaker / Craftsman / Related Services, Busse / Swamprat / Scrapyard Knives For Sale, For Sale: Traditionals, Slipjoints, "Old Timey", International (Non-US) For Sale & Trade Forums. Once your Damascus is sanded to the correct grit, thoroughly wash it with alcohol and pat dry with a clean rag. Adding HCl acid can restore the cutting ability of the FeCl3.